Beyem Cril Polisiloxano

BEYEM CRIL is a pigment-coloured acrylic mortar with high strength and lightfastness pigments for decorative finishing of the BEYEM SATE system.

It has three finishes:

• Thick 2.5 kg/m²
• Thin 2 kg/m²
• TX 2-2.5 kg/m²

It provides resistant, elastic, waterproof finishes with high covering power. It has polysiloxane additives that give it a high water-repellent power and high breathability. It can be applied on large surfaces and working joints.

• Maximum impermeability
• Permeable to water vapour
• Flexible: high deformation capacity.
• Low modulus of elasticity
• Semi-elastic (anti-cracking)
• Excellent workability
• High adhesion
• Low maintenance
• Ready to use
• Different finishes: Thin, TX, Coarse
• Includes anti-mould preservatives

Decorative coating for SATE. Anti-cracking system in conjunction with other BEYEM products./p>

The useful supports for the application of BEYEM CRIL are:

BEYEM SATE system:

• BEYEM ADHETERM, BEYEM CRIL FONDO

Other BEYEM products

• BEYEM R1T RENODUR, etc… (Sistema antifisuras)
• BEYEM S-GRIS, BEYEM S-BLANCO, BEYEM IMPER.

The above-mentioned substrates must be sound, clean, free of poorly adhering parts or substances that may hinder adhesion. All substrates must have adequate flatness. The substrate must not have any clear problems of dampness and, where applicable, must have completed its curing shrinkage and its maturing period must have been respected.

The substrate must be clean, clean, free from bad adhering parts or substances that may hinder adhesion.

After at least 6 hours from the application of Beyem Cril Fondo, apply Beyem Cril Polisoloxano with a stainless steel trowel, spreading the product uniformly over the surface. Once the product has lost its tackiness on the tool, proceed to finish the surface with a trowel or trowel.

• Do not apply at temperatures below 5°C or above 30°C, or when humidity exceeds 75%.
• Do not apply if there is a risk of frost, rain, strong winds or direct sunlight.
• Keep containers tightly closed after use.
• Conditions of high humidity and/or low temperatures may prolong drying time and cause loss of colour uniformity. The same may occur with high temperatures or strong winds, as these reduce drying time. This is particularly important if the work extends across different seasons or if there is a break in the work. The execution of the work should be planned to minimise this risk.
• Avoid using different batches on the same surface; if this is not possible, it is advisable to mix the contents of the second container with the first once 50% of the first has been used. This will prevent any slight variations in shade between batches from affecting the final result.
• It is recommended to cover the scaffolding with fabric or tarpaulins to protect the surface after application from wind, rain or intense sunlight (approx. 2 days in favourable weather conditions).
• Avoid leaving a section half-finished to prevent joints. Use working joints if necessary.
• This product is not suitable for protecting horizontal or sloping surfaces where water may pool.
• We do not recommend using colours with a solar radiation absorption coefficient (α) greater than 0.7, unless the façade is permanently shielded from solar radiation.
• Protect the upper edges of the cladding against rainwater penetration.
• Due to the existence of a large number of mould species and varying climatic conditions, in some cases the additives used cannot guarantee the complete elimination or prevention of the proliferation over time of certain plant microorganisms.
• Observe expansion joints.
• Product recommended for expert users.

BEYEM CRIL Polisiloxano is packaged in 15 L. plastic buckets.
Storage: 24 months in sealed original packaging, at non-extreme temperature and humidity. Keep out of direct sunlight.

Tools and tools are easily cleaned with water before the paste has hardened. Cured or hardened product can only be removed by mechanical means.

The completion of the Beyem External Thermal Insulation System (SATE) will be carried out with Beyem Cril coloured acrylic coating, from the company Rodacal Beyem, with ETE number 21/0061 under EAD 040083-00-0404. The yield shall be ≈ 2.0-2.5 kg/m2. The substrate shall be clean, sound, compact and dimensionally stable. Expansion joints shall be respected, where applicable, as well as the manufacturer’s general installation instructions.

For any information regarding safety issues in the use, handling, storage and disposal of chemical residues, users should refer to the most recent version of the MSDS for the product. Disposal of the product and its packaging must be carried out in accordance with current legislation and is the responsibility of the final consumer of the product.